Lefatše le sa tloaelehang oxide yttrium oxide phofo 1314-36-9
Kenyelletso e khutšoane ea Yttrium Oxide
Foromo (Y2O3)
Nomoro ea CAS: 1314-36-9
Bohloeki: 99.999%
SSA: 25-45 m2 / g
'Mala: bosoeu
Morphology: chitja
Boima ba Bongata: 0.31 g/cm3
Boima ba 'Nete: 5.01 g/cm3
Boima ba 'mele: 225.81
Sebaka se qhibilihang: likhato tsa 2425 celsium
Ponahalo: Phofo e tšoeu
Solubility: Ha e qhibilihe ka metsing, e qhibiliha ka mokhoa o itekanetseng ho li-mineral acid tse matla
Botsitso: E batla e le hygroscopic
Sesebelisoa sa Yttrium oxide
1: Yttrium Oxide, eo hape e bitsoang Yttria, high purity Yttrium Oxides ke lisebelisoa tsa bohlokoa ka ho fetisisa bakeng sa lihlopha tse tharo tsa Rare Earth phosphors tse fanang ka 'mala o mofubelu thelevisheneng ea mebala le li-tubes tsa k'homphieutha.
2:Indastering ea optical, Yttrium Oxide e sebelisetsoa ho hlahisa Yttrium-Iron-Garnets, e leng li-filters tse sebetsang hantle haholo tsa microwave.
3: Bohloeki bo tlase ba Yttrium Oxide bo sebelisoa haholo ka lirafshoa tsa elektroniki. E sebelisoa haholo ho etsa li-phosphor tsa Eu:YVO4 le Eu:Y2O3 tse fanang ka 'mala o mofubelu ka li-tubes tsa litšoantšo tsa TV tsa mebala.
4: Yttrium Oxide e boetse e sebelisetsoa ho etsa Yttrium-Iron-Garnets, e leng li-filters tse sebetsang hantle haholo tsa microwave.
| ITEM | LIEKETSENG TS'OANELO | LIPOLELO TSA TEKO | ||||||
| Y2O3/TREO(%,min) | 99.995 | 99.999 | ||||||
| TREO(%,min) | 98 | 98.38 | ||||||
| Boholo ba Karolo | 30-60nm, 1.0-2.0um, 0.3-0.6um, 0.6-1.0um | Ikamahanye | ||||||
| RE Litšila(/REO,%) | ||||||||
| La2O3 | ≤0.0005 | ≤0.0001 | ||||||
| CeO2 | ≤0.0005 | ≤0.0001 | ||||||
| Pr6O11 | ≤0.0002 | ≤0.0001 | ||||||
| Nd2O3 | ≤0.0002 | ≤0.0001 | ||||||
| Sm2O3 | ≤0.0002 | ≤0.0001 | ||||||
| Eu2O3 | ≤0.0002 | ≤0.0001 | ||||||
| Gd2O3 | ≤0.0002 | ≤0.0001 | ||||||
| Tb4O7 | ≤0.0002 | ≤0.0001 | ||||||
| Dy2O3 | ≤0.0002 | ≤0.0001 | ||||||
| Ho2O3 | ≤0.001 | ≤0.0001 | ||||||
| Er2O3 | ≤0.001 | ≤0.0001 | ||||||
| Tm2O3 | ≤0.0001 | ≤0.00002 | ||||||
| Yb2O3 | ≤0.0001 | ≤0.00002 | ||||||
| Lu2O3 | ≤0.0001 | ≤0.00002 | ||||||
| LOI | ≤2% | |||||||